德国巴斯夫+Polysulfone (PSU)S 6010

详情描述：

德国巴斯夫Polysulfone (PSU)S 6010is an unreinforced, high molecular weight injection-molding and extrusion grade with excellent chemical resistance (stress crack resistance) and good solubility in typical solvents (N-Methylpyrrolidone, Dimethylacetamide, Dichlormethane) used e.g. in the production of membranes or coatings, with reduced oligomer content. It conforms to FDA requirements of 21 CFR 177.1655
德国巴斯夫Polysulfone (PSU)S 6010热性能参数如下：
线形热膨胀系数 - 流动
53.0 ?m/m-?C
@Temperature 23.0 - 80.0 ?C
29.4 ?in/in-?F
@Temperature 73.4 - 176 ?F
60.0 ?m/m-?C
@Temperature 140 - 180 ?C
33.3 ?in/in-?F
@Temperature 284 - 356 ?F
高工作温度, Air
180 ?C
356 ?F
short cycle operations
载荷下热变形温度(1.8 MPa)
175 ?C
347 ?F
ISO 75-2
玻璃化转变温度，Tg
187 ?C
369 ?F
10 K/min; ISO 11357-1/-3
德国巴斯夫Polysulfone (PSU)S 6010加工工艺参数如下：
加工（熔体）温度
330 - 390 ?C
626 - 734 ?F
模具温度
120 - 160 ?C
248 - 320 ?F
德国巴斯夫Polysulfone (PSU)S 6010电气性能参数如下：
体积电阻率
>= 1.00e 13 ohm-cm
>= 1.00e 13 ohm-cm
IEC 60093
表面电阻
>= 1.00e 14 ohm
>= 1.00e 14 ohm
IEC 60093
介电强度
37.0 kV/mm
940 kV/in
IEC 60243-1 3
相比耐漏电起痕指数(CTI)
125 V
125 V
Test Liquid A; IEC 60112